分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-26
摘要: The formation of Cu precipitates in Fe-0.3%Cu binary model alloy after hydrogen ion irradiation at 400 was investigated by positron annihilation spectroscopy based on slow positron beam. In order to study the effect of elevated temperature for the Cu precipitates, the annealing treatment at 400 in Fe-0.3%Cu alloy was also investigated. The S-parameters of specimens increased with the irradiation dose increased, especially in the damage peak region. H+ implantation produced a large number of vacancy-type defects in Fe-0.3%Cu alloy. Compared to the unirradiated samples, the irradiated specimens show an overall major increase in W parameter values. Experimental results indicate that Cu precipitates formed easily under lower irradiation dose at elevated temperature. No obvious Cu precipitates formed when Fe-0.3%Cu alloy was annealed for 2h at 400 .
分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-23
摘要: The effect of annealing on VmHn complexes and Cu precipitate behaviors in hydrogen ion irradiated Fe and Fe-0.3%Cu alloys was investigated by positron annihilation spectroscopy using a slow positron beam. The results of S parameters indicated that the room temperature irradiation was benefit for the formation of the VmHn complex compared to the elevated temperature irradiation. The S-W results confirmed the formation of Cu precipitates in Fe-0.3%Cu even at the irradiation dose of 0.1 dpa. The formation of the evident S value peaks in the damage region after annealing treatment suggested that the VmHn complexes were broken and a larger of hydrogen atoms were escaping. The residual vacancy defects would migrate towards both the surface region and the opposite direction with the increasing annealing temperature.