分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-26
摘要: The correlation between Cu precipitates and vacancy-like defects in three Fe-Cu model alloys, Fe-0.15%Cu, Fe-0.3%Cu and Fe-0.6%Cu, irradiated at 400 °C with hydrogen ions at doses from 0.045 to 0.45 dpa, were revealed by positron annihilation spectroscopy. The formation of vacancy-like defects surrounded by tiny Cu precipitates induced the increment of the S and W parameters after irradiation. The peak value of the relative W parameter (ΔW/W), as the high momentum information on Cu precipitates, located in the track region and decreased with irradiation dose increased from 0.045 dpa to 0.45 dpa. The information on high momentum depended on the coverage fraction of the defects by Cu atoms. The effect of the irradiation dose, the irradiation depth and the Cu content on the Cu coverage fraction of the defects has been investigated in the present work
分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-26
摘要: The formation of Cu precipitates in Fe-0.3%Cu binary model alloy after hydrogen ion irradiation at 400 was investigated by positron annihilation spectroscopy based on slow positron beam. In order to study the effect of elevated temperature for the Cu precipitates, the annealing treatment at 400 in Fe-0.3%Cu alloy was also investigated. The S-parameters of specimens increased with the irradiation dose increased, especially in the damage peak region. H+ implantation produced a large number of vacancy-type defects in Fe-0.3%Cu alloy. Compared to the unirradiated samples, the irradiated specimens show an overall major increase in W parameter values. Experimental results indicate that Cu precipitates formed easily under lower irradiation dose at elevated temperature. No obvious Cu precipitates formed when Fe-0.3%Cu alloy was annealed for 2h at 400 .